Barra Hexagonal 12L14 / Hexagonal Steel Bar 12L14 / Trefilado Hexagonal 12L14
12L14 - COLD DRAWN ROUND ROD
Cold Drawn Round 12L14 Carbon Steel Bar/Rods are best known for their excellent machinability due to its added Lead content.
12L14 Cold Drawn Steel Rods are frequently used to fabricate high speed machinery. It has very high machinability and low weldability, but it can be bent, riveted or crimped.
1.12L14 chemical composition
| Element |
Content (%) |
| Iron, Fe |
97.91 - 98.7 |
| Manganese, Mn |
0.85 - 1.15 |
| Sulfur, S |
0.260 - 0.35 |
| Lead, Pb |
0.15 - 0.35 |
| Carbon, C |
0.15 |
| Phosphorous, P |
0.040 - 0.090 |
2.12L14 physical property
| Properties |
Metric |
Imperial |
| Tensile strength |
540 MPa |
78300 psi |
| Yield strength |
415 MPa |
60200 psi |
| Bulk modulus (typical for steel) |
140 GPa |
20300 ksi |
| Shear modulus (typical for steel) |
80.0 GPa |
11600 ksi |
| Elastic modulus |
190-210 GPa |
27557-30458 ksi |
| Poisson's ratio |
0.27-0.30 |
0.27-0.30 |
| Elongation at break |
10% |
10% |
| Reduction of area |
35% |
35% |
| Hardness, Brinell |
163 |
163 |
| Hardness, Knoop (converted from Brinell hardness) |
184 |
184 |
| Hardness, Rockwell B (converted from Brinell hardness) |
84 |
84 |
| Hardness, Vickers (converted from Brinell hardness) |
170 |
170 |
| Machinability (based on 100 machinability for AISI 1212 steel) |
160 |
160 |
3.Sizes we can supply for 12L14 cold drawn steel bars:
| Shapes |
Sizes |
Processing |
| Steel Round Bar |
5mm to 63.5mm |
Cold Drawn |
| Steel Round Bar |
63.5mm-120mm |
smooth-turned and polished. |
| cold drawn steel square bar |
5*5mm to 120*120mm |
Cold Drawn |
| cold drawn steel hex bar |
5mm to 120mm |
Cold Drawn |
| cold drawn steel hexagonal bar |
5mm to 120mm(side to side) |
Cold Drawn |
4..Advantages of cold drawn steel bar:
1.It can remove the Size and Section which provides Tighter tolerances which Reduces machining losses.
2.It can remove the Steel Surface Finish which Reduces surface machining & improves quality.
3.It can remove the Straightness which Facilitates automatic bar feeding in CNC.
4.It can increase the Mechanical Properties which Can reduce the need for hardening.
5.It can improve the Machinability and Productivity which Enables higher machining feeds, high tool life, yield & speeds and improved machined finish.
5.Delivery time : 7days for stocks, within 30 days for new production ones.
6.Payment : TT, LC
7.MOQ: 2tons per sizes
12L14 FREE CUTTING STEEL,12L14 COLD DRAWN STEEL BARS, 12L14 FREE CUTTING STEEL BAR, 12L14 ROD, 12L14 PROPERTY, 12L14 CHEMICAL COMPOSITION, 12L14,ASTM 1215 DIFFERENT, 12L14 COLD DRAWN STEEL BAR MANUFACTURER. 12L14 FREE CUTTING STEEL,12L14 COLD DRAWN STEEL BARS, 12L14 FREE CUTTING STEEL BAR, 12L14 ROD, 12L14 PROPERTY, 12L14 CHEMICAL COMPOSITION, 12L14,ASTM 1215 DIFFERENT, 12L14 COLD DRAWN STEEL BAR MANUFACTURER.
Audited Supplier 
){kind=link}
){kind=link}