ASTM A193 Grade B7 Steel4140 Heat-Treated Chromium-Molybdenum Plain Steel Bar for Threaded Rods and Anchor Bolts

• Type: Alloy Steel Bar
• Standard: AISI, ASTM, GB, JIS, DIN, BS
• Technique: Q&T (Quenched & Tempered)
• Application: Structural Steel Bar, Tool Steel Bar, Die Steel Bar
• Surface Treatment: A193 B7 4140 Q&T Steel
• Alloy: Alloy
• Model NO.: ASTM A193 Grade B7 plain steel bar
• Special Use: Mold Steel, Free Cutting Steel, Cold Heading Steel
• Grade: ASTM A193 B7 4140
• Condition: Q&T Steel Round Bars
• Raw Material: 4140 Qt Bars
• Sizes: M8-M120
• Applications: Threaded Rod, Ahchor Bolts, Studs, Bolts
• MOQ: 2tons
• Length: 3660mm, 6m or as Required
• Products: A193 B7 Q&T Steel Round Bars
• A193 B7 Yield Strength: Min 720MPa
• A193 B7 Tensile Strength: Min 860MPa
• A193 B7 Elongation: 16% Min
• Surface: Smooth
• Transport Package: Standard Export Packing
• Specification: M12-M100
• Trademark: Laiwu Xincheng
• Origin: China
• HS Code: 72283090
• Production Capacity: 3000tons/Month

Product Description

ASTM A193 Grade B7 Steel4140 Heat-Treated Chromium-Molybdenum Plain Steel Bar for threaded rods and anchor bolts

ASTM A193 Grade B7 Chromium Molybendum steel, normally AISI 4140, heat treated to 28-32Rockwell Hardness, 125,000 PSI tensile strength, 105, 000 PSI yield. It will hold it's strength to 1000 degrees F.

ASTM A193 Grade B7 Threaded Rod is a kind of high strength and heat resistant threaded rod manufactured from 4140/4142 quenched and tempered alloy steel for high temperature or high pressure service, used by the plumbing and contracting trade in maintenance departments to secure pressure tanks, valves, and flanges.

1.A193 B7 round bar Chemical composition: (raw material aisi 4140 )

Grade	C	Si	Mn	P	S	Cr	Mo
SAE 4140	0.37-0.49	0.15-0.35	0.65-1.1	Max0.035	Max0.04	0.75-1.20	0.15-0.25

2.A193 B7 Round Bar Properties:

Tensile Strength	Yield Strength	Elongation	Reduction Area	Hardness
Mpa	MpA	%	%	HRC
min860	min720	min12	min50	max35

3.Sizes of A193 B7 QT steel bars we can supply :
Hot rolled steel round bar :M12-M310
Hot Rolled & QT (Quenched and tempered): M12-M120
Cold Drawn&QT (Quenched and tempered):M6-M120
Peeled+QT(Quenched and tempered):M20-M120

4.A193 B7 QT bars packing : surface oiled+ Woven cloth 
5.Straightness of QT bars: Max 1mm/m (important )
6.Payment terms: T/T or L/ C
(1)30% paid by T/T and rest 70% by T/T upon the copy of B/B.
(2)100% irrevocable L/C at sight
7.Delivery time:within 7 days after your deposit or L/C.
8.Mark: including steel material, heat No., pieces, weight, date and so on.
9.Quality control
1.Process for Steel round bar
Blast Furnance→ Molten Iron Pretreatment→Converter→LF→VD/RH→ContinuousCasting→Hot Rolling(KOCKS)→ Heat Treatment→ UT Inspection→Finish Product
EAF→LF→VD/RH→ Continuous Casting→Hot Rolling(KOCKS)→ Heat Treatment→ UT Inspection→ Finish Product
2.Grain Sizes:5-8
3.Surface condition: The surface of the bar shall be free cracks, scar and wrinkles at affect the use of the billets. 
4.The mill test certificate shall show the chemical composition, and it is guaranteed that the chemical composition shall be within the limit stipulated in the contract