AISI 4140 42CrMoA En19 1.7225 Heat Treated QT Steel Round Bar
AISI 4140 steel has good machinability. Operations such as turning, hobbing, drilling, sawing, broaching, tapping and milling can be easily performed using the recommendations provided by the machine's manufacturer for ideal tool type-feeds and speeds.
| ASTM A29/29M |
C |
Si |
Mn |
Cr |
Mo |
P |
S |
| 4140 |
0.38~0.43 |
0.15~0.35 |
0.75~1.00 |
0.80~1.10 |
0.15~0.25 |
≤0.035 |
≤0.040 |
| DIN WN-r |
C |
Si |
Mn |
Cr |
Mo |
P |
S |
| 1.7225 |
0.38~0.45 |
≤0.40 |
0.60~0.90 |
0.90~1.20 |
0.15~0.30 |
≤0.035 |
≤0.035 |
| GB/T |
C |
Si |
Mn |
Cr |
Mo |
P |
S |
| 42CrMo |
0.38~0.45 |
0.17~0.37 |
0.50~0.80 |
0.90~1.20 |
0.15~0.25 |
≤0.030 |
≤0.030 |
| BS |
C |
Si |
Mn |
Cr |
Mo |
P |
S |
| 708M40 |
0.36~0.44 |
0.10~0.35 |
0.70~1.00 |
0.90~1.20 |
0.15~0.25 |
≤0.035 |
≤0.035 |
| JIS |
C |
Si |
Mn |
Cr |
Mo |
P |
S |
| SCM440 |
0.38~0.43 |
0.15~0.35 |
0.60~0.85 |
0.90~1.20 |
0.15~0.30 |
≤0.030 |
≤0.030 |
AISI 4140 42CrMoA EN19 heat treated steel round bar
heat treatments of the AISI 4140 Chrome-Molybdenum High Tensile Steel
Forging
Stress relieving
Annealing
Normalizing
Nitriding
Tempering
Flame and induction hardening
Hardening
Supply Size range
| Delivery condition |
Diameter ranges |
| Hot tolled |
M12-M310 |
| Hot rolled+Q&T(Quenched and tempered) |
M12-M310. |
| Cold drawn +Q&T(Quenched and tempered) |
M10-M100 |
| Peeled / Peeled+Q&T |
M10-M100 |
| Forged/Forged+Heat treatment. |
M250-M1000 |
AISI 4140 equivalent material
♦JAPAN♦ : JIS SCM440 alloy steel
♦GERMANY♦ : DIN WN-r 1.7255 / 42CrMo4 steel alloy
♦CHINA♦ : GB 42CrMo steel
♦BRITISH♦ : BS 708M40
Payment terms: T/T or L/ C
(1)30% paid by T/T and rest 70% by T/T upon the copy of B/B.
(2)100% irrevocable L/C at sight
Delivery time:within 7 days after your deposit or L/C.
Trade term: FOB CFR CIF
Port of loading:Qingdao , China
Mark: including steel material, heat No., pieces, weight, date and so on.
Quality control
1.Process for Steel round bar
Blast Furnance→ Molten Iron Pretreatment→Converter→LF→VD/RH→ContinuousCasting→Hot Rolling(KOCKS)→ Heat Treatment→ UT Inspection→Finish Product
EAF→LF→VD/RH→ Continuous Casting→Hot Rolling(KOCKS)→ Heat Treatment→ UT Inspection→ Finish Product
2.Grain Sizes:5-8
3.Surface condition: The surface of the bar shall be free cracks, scar and wrinkles at affect the use of the billets.
4.The mill test certificate shall show the chemical composition, and it is guaranteed that the chemical composition
shall be within the limit stipulated in the contract