ASTM A193 316L STAINLESS STEEL FASTENERS EQUIVALENT GRADES :
EQUIVALENT GRADE TO SS316 L
| STANDARD |
UNS |
WERKSTOFF NR. |
JIS |
GOST |
BS |
AFNOR |
EN |
| SS 316L |
S31603 |
1.4404 / 1.4435 |
SUS 316L |
03Ch17N14M3 / 03Ch17N14M2 |
316S11 / 316S13 |
Z3CND17‐11‐02 / Z3CND18‐14‐03 |
X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
A193 STAINLESS STEEL 316L FASTENERS SPECIFICATIONS :
(316L THREADED ROD, STUD BOLTS, NUTS, WASHERS ETC)
| Specifications : ASTM A193 B8, B8M, B6, B8T, B8C, A194 G8, 8M, 8C, 8T |
| Size Range : M3 to M100, 1/4" to 4" |
| Variants : 316L |
| Standard : ASTM,DIN, BS,GB, IS and all International Standards |
| Diameter : 12 mm dia to 72 mm dia |
| Length : can be fixed and customized |
CHEMICAL COMPOSITION OF ASTM A193 STAINLESS STEEL 316L FASTENERS :
| Grade |
C |
Ni |
Mn |
S |
Cr |
Si |
P |
Mo |
N |
| SS 316L |
min. |
- |
10.0 |
- |
- |
16.0 |
- |
- |
2.00 |
- |
| max. |
0.08 |
14.0 |
2.00 |
0.03 |
18.0 |
0.75 |
0.045 |
3.00 |
0.10 |
MECHANICAL PROPERTIES OF STAINLESS STEEL 316L FASTENERS :
| Grade |
Yield Strength 0.2% Proof (MPa) min |
Tensile Strength (MPa) min |
Elongation (% in 50mm) min |
Hardness |
| Rockwell B (HR B) max |
Brinell (HB) max |
| SS 316L |
170 |
485 |
40% |
95 |
217 |
Stainless Steel 316L Stud Bolts Supplier, Stainless Steel 316L Studs, Stainless Steel 316 Stud Bolt, UNS S31600 Threaded Rod, SS 316/316L Double End Stud Bolt Manufacturer
SS304 Stainless Threaded Rods,Stud Bolts
SS316L Stainless Threaded Rods,Stud Bolts
A194, Grade8, Grade 8M Heavy Hex Nuts
ASTM A193 B8 Threaded rod.
ASTM A193 B8M CL2 Threaded rod, Stud bolts with nuts
ASTM A193 Bolts Studs and Rods
SS 316 / 316L Stud Bolts, which has high corrosion resistance and strength. Stainless Steel 316 Stud Bolts is typically used for elevated temperature applications. Stainless Steel 316L Stud Bolts is the low carbon version which minimizes carbide precipitation and improves weldability. The lower nickel content of SS 316 Stud Bolts improves resistance to sulfur attack at high temperatures. SS 316L Stud Bolts is employed for parts requiring both corrosion and heat resistance and oxidation resistance up to 2000 Degree F